產(chǎn)品詳情
| 化學(xué)成分 | |||||||
| C5210的典型化學(xué)成分 | |||||||
| Cu | Sn | P | Fe | Pb | Cu+Sn+P | ||
| Typical | Bal | 8.0 | 0.15 | ≤0.10 | ≤0.05 | ≥99.7 | |
| 物理性質(zhì) | |||||||
| C5210的物理性質(zhì) | |||||||
| 電導(dǎo)率 | 12 %IACS(@20℃) | ||||||
| 比電阻 | 144 nQ ·m(@20℃) | ||||||
| 熱導(dǎo)率 | 63 W/mK | ||||||
| 熱膨脹系數(shù) | 18.2 ×10-6(20 to 300℃) | ||||||
| 楊氏模量 | 110 kN/mm2 | ||||||
| 密度 | 8.80 g/cm3 | ||||||
| 機械性能 | |||||
| 機械性能 | |||||
| Temper |
抗拉強度 (N/mm2) |
0.2%偏移屈服強度 (N/mm2) |
伸長率 (%) |
疲勞強度 (N/mm2) |
|
|
H |
Range | 590～705 | ≥20 | ||
| Hyper | 636 | 565 | 33.4 | 400 | |
| Conventional | 625 | 528 | 28.9 | 300 | |
|
EH |
Range | 685～785 |
≥11 |
||
| Hyper | 729 | 688 | 22.1 | 450 | |
|
Conventional |
724 | 667 | 19.0 | 350 | |
|
SH |
Range | 735～835 | ≥9 | ||
| Hyper | 790 | 760 | 17.8 | 400 | |
| Conventional | 764 | 710 | 18.1 | 350 | |
|
ESH |
Range | 770～885 | ≥5 | ||
| Hyper | 853 | 823 | 12.0 | 400 | |
| Conventional | 813 | 786 | 12.6 | 300 | |
C5210R-SH磷青銅帶的性能特點
C5210R-SH磷青銅帶具有眾多出色的性能特點。首先，它具備卓越的耐蝕性，在稀硫酸、鹽酸和脂肪酸等腐蝕環(huán)境中表現(xiàn)優(yōu)異3。其次，機械性能十分出色，擁有高強度、良好的彈性和出色的耐磨性，能夠適應(yīng)各種復(fù)雜的機械應(yīng)用場景2。此外，它還具有良好的切削性能，這使得它能夠被用于制造需要精確尺寸的零件3。同時，C5210R-SH磷青銅帶易于焊接和纖焊，這為其在組裝過程中提供了極大的便利2。而且，它在大氣、淡水和海水中均有良好的耐蝕性，適用范圍廣泛3。其硬度通?！?85HB，展現(xiàn)出較高的硬度水平3。
C5210R-SH磷青銅帶的應(yīng)用領(lǐng)域
C5210R-SH磷青銅帶在多個領(lǐng)域都有廣泛的應(yīng)用。在電子行業(yè)，它常被用于制造導(dǎo)線、連接器和電路板等電子元器件7。在機械工程領(lǐng)域，由于其高強度和耐磨性，適用于制造需要高強度和耐磨性的機械零件和結(jié)構(gòu)件，例如齒輪、軸等8。在化工領(lǐng)域，其卓越的耐蝕性使其成為制造耐受腐蝕介質(zhì)的容器和管道等的理想材料