產(chǎn)品詳情
| 化學(xué)成分 | |||||||
| C5210的典型化學(xué)成分 | |||||||
| Cu | Sn | P | Fe | Pb | Cu+Sn+P | ||
| Typical | Bal | 8.0 | 0.15 | ≤0.10 | ≤0.05 | ≥99.7 | |
| 物理性質(zhì) | |||||||
| C5210的物理性質(zhì) | |||||||
| 電導(dǎo)率 | 12 %IACS(@20℃) | ||||||
| 比電阻 | 144 nQ ·m(@20℃) | ||||||
| 熱導(dǎo)率 | 63 W/mK | ||||||
| 熱膨脹系數(shù) | 18.2 ×10-6(20 to 300℃) | ||||||
| 楊氏模量 | 110 kN/mm2 | ||||||
| 密度 | 8.80 g/cm3 | ||||||
| 機(jī)械性能 | |||||
| 機(jī)械性能 | |||||
| Temper |
抗拉強(qiáng)度 (N/mm2) |
0.2%偏移屈服強(qiáng)度 (N/mm2) |
伸長(zhǎng)率 (%) |
疲勞強(qiáng)度 (N/mm2) |
|
|
H |
Range | 590～705 | ≥20 | ||
| Hyper | 636 | 565 | 33.4 | 400 | |
| Conventional | 625 | 528 | 28.9 | 300 | |
|
EH |
Range | 685～785 |
≥11 |
||
| Hyper | 729 | 688 | 22.1 | 450 | |
|
Conventional |
724 | 667 | 19.0 | 350 | |
|
SH |
Range | 735～835 | ≥9 | ||
| Hyper | 790 | 760 | 17.8 | 400 | |
| Conventional | 764 | 710 | 18.1 | 350 | |
|
ESH |
Range | 770～885 | ≥5 | ||
| Hyper | 853 | 823 | 12.0 | 400 | |
| Conventional | 813 | 786 | 12.6 | 300 | |
C5210R-EH磷青銅帶具有一系列出色的性能特點(diǎn)。首先，它的強(qiáng)度較高，能夠滿足多種高強(qiáng)度應(yīng)用的需求2。同時(shí)，具備良好的彈性，在受到外力作用后能夠迅速恢復(fù)原狀3。 其耐磨性也表現(xiàn)優(yōu)異，這使得它在長(zhǎng)期使用過(guò)程中能夠保持較好的表面質(zhì)量和尺寸精度3。 在焊接和纖焊方面，C5210R-EH磷青銅帶易于操作，能夠?qū)崿F(xiàn)牢固可靠的連接3。 在耐蝕性方面，無(wú)論是在大氣、淡水還是海水中，都能展現(xiàn)出良好的耐腐蝕性能，有效延長(zhǎng)使用壽命3。 此外，它的可切削性良好，便于進(jìn)行各種機(jī)械加工操作3。 而且，C5210R-EH磷青銅帶的導(dǎo)電率為12%IACS(@20℃)，電阻率為144nΩ?m(@20℃)，導(dǎo)熱系數(shù)為63W/mK，線性膨脹系數(shù)為18.2×10-6/K(20 to 300℃)，縱向彈性模量為110GPa，密度為8.80g/cm34。
C5210R-EH磷青銅帶的應(yīng)用領(lǐng)域
C5210R-EH磷青銅帶在眾多領(lǐng)域都有廣泛的應(yīng)用。在電子行業(yè)，它常被用于制造導(dǎo)線、連接器和電路板等電子元器件，因其良好的導(dǎo)電性和穩(wěn)定性能夠保障電子設(shè)備的正常運(yùn)行7。 在太陽(yáng)能光伏領(lǐng)域，被用于制造太陽(yáng)能電池的電極和連接器等部件，充分發(fā)揮其耐腐蝕性和導(dǎo)電性能9。 在航空航天領(lǐng)域，由于其高強(qiáng)度和輕質(zhì)特性，被用于制造飛機(jī)和火箭的零部件